Photocatalytic oxidation of gaseous benzene over nanosized TiO_2 prepared by solvothermal method
扫码查看
点击上方二维码区域,可以放大扫码查看
原文链接
NETL
NSTL
Nanosized TiO_2 particles were prepared by solvothermal method using tetrabutyl titanate as precursor, ethanol and water as solvents, and a facile immobilization method of nanosized TiO_2 particles on woven glass fabric was developed. The samples obtained under various preparation conditions were characterized by means of thermo gravimetric analysis (TG) and differential scanning calorimetry (DSC), X-ray diffraction (XRD), transmission electron microscopy (TEM), high resolution-transmission electron microscopy (HR-TEM), and Brunauer-Emmett-Teller (BET). The results show that the cube-shape of TiO_2 prepared by solvothermal method has good crystallinity of (101) surface, higher thermal stability and large specific surface area. Scanning electron microscopy (SEM) images confirmed that the immobilized TiO_2 film was uniformly distributed and clung to the substrate firmly. The photocatalytic activity of the catalysts was tested using photocatalytic oxidation of gaseous benzene. The results show that the TiO_2 calcined after solvothermal treatment suffers from lower specific surface area, and hence decreases its photocatalytic activity. The photocatalytic activities of the TiO_2 by solvothermal treatment with or without calcination in degradation 400 mg/m~3 benzene are 3.7 and 4.1 times as high as catalyst without solvothermal treatment, respectively.