Fatigue Crack Initiation and Growth in a High Loaded Bolted Bar Connection
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NETL
NSTL
The fatigue crack initiation and growth in a high loaded bolted bar connection made of high strength steel S1100Q is presented. The material parameters for the fatigue crack initiation σ_t', ε_f', b and c are determined using low cycle fatigue test according to ASTM E 606 standard. The fracture mechanics parameters C and m are determined according to ASTM E 647 standard. Based on low cycle fatigue parameters the computational analysis is performed to determine the number of stress cycles required for the fatigue crack initiation. The remain service life up to the final failure is than determined using the known parameters C and m and calculated stress intensity factor, where 3D numerical analysis is performed. The bolted bars are also experimentally tested. Comparison of computational and experimental results shows a reasonable agreement.
fatiguefgracture mechanicsstrain life approachnumerical analysis
NETL
NSTL