The Effects of Sintering Temperature Variations on Some Physical Properties of Al_2O_3-SiO_2-PbO-MgO Laminated Tape System
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NETL
NSTL
Trans Tech Publications Ltd
An Al_2O_3-SiO_2-PbO-MgO laminated tape system was prepared to investigate the dependence of some physical properties on various sintering temperatures, 840 ℃, 880 ℃, 920 ℃ and 960 ℃. The results show that the effect of the increasing sintering temperatures was a fluctuating in the density value of the laminates. It was also observed that the dielectric constant and dielectric loss showed the lowest value for the sintering temperature of 880 ℃. SEM micrographs of the laminate samples shows a mixture of grain sizes and the samples had a combination of small and large pores with the average grain size around 2.20-2.64 μm.
sinteringlaminatedtapemicrostructuredielectric
Rosidah Alias、Azmi Ibrahim、Sabrina Mohd Shapee、Zulkifli Ambak、Zulfadli Mohamed、Yusoff Muhammad Redzuan Saad、Che Seman Mahmood、Megat Harun Al Rashid Megat Ahmad
展开 >
Microelectronics and Nano Technology Program, TM Research & Development Sdn. Bhd., TMR&D Innovation Centre, Lingkaran Teknokrat Timur, 63000 Cyberjaya, Selangor,Malaysia
Materials Technology Group (MTEC), Industrial Technology Division, Malaysian Nuclear Agency, Bangi, 43000 Kajang, Selangor, Malaysia
NETL
NSTL
Trans Tech Publications Ltd