Friction Stir Processing (FSP) of As-Cast AA5083 for Grain Refinement and Superplasticity
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NETL
NSTL
Trans Tech Publications Ltd
Multi-pass FSP was conducted on continuously-cast (CC) AA5083 materials in the as-cast condition. Stir zone grains were refined to ～1.0 - 3.5μm in size and highly superplastic response was obtained during tension testing of the as-processed materials at 450℃ (>1200 pct. elongation at 10~(-1) s~(-1)). Current models of recrystallization do not predict adequately the highly refined grains and predominantly random textures that are observed in stir zones. Grain refinement during FSP is accompanied by refinement and redistribution of non-deforming constituents in the absence of particle fracture. The mechanics of the homogenization process remain to be established and requirements for redistribution mechanisms will be summarized. Comparison reveals that results from FSP of the as-cast material are superior to those attained in conventional processing.
NETL
NSTL
Trans Tech Publications Ltd