首页|Preparation of Porous Mullite Ceramics by Fly Ash/Al Compositions
Preparation of Porous Mullite Ceramics by Fly Ash/Al Compositions
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NETL
NSTL
Trans Tech Publications Ltd
Porous mullite was prepared from a reactive mixture of Al metal powder and the fly ash produced by power plant. The sintering ceramics was characterized for the pore structure and phase identification studies. It was found that the sintered specimen expands at first (1300-1400℃) and then shrinks which was correspondence to the changing of open porosity. The expansion was attributed to the fact that the alumina produced from the oxidation reaction of Al powder made the volume larger than the starting mixtures. At 1550℃, it was inferred that the alkaline element in the fly ash made the mullite decomposed then destroyed the mullite structure. The SEM photographs suggested us that the pore diameter of the sintered ceramics might be adjusted by adding Al powder with different grain sizes. Moreover, because of the rod-like mullite produced in the pores, Mg metal addition could develop the further modification of the pore structure with similar porosity (47% at 1400℃/4h) compared with that (53%) with Owt % Mg metal powders.
porous mullitefly ashAl powderMg powder
Qihui Jia、Jiachen Liu、Jiping Guo、Xiongwei Du、Zhongjie Wang、Wenjun Wang
展开 >
School of Materials Science and Engineering of Tianjin University, Key Lab of Advanced Ceramics and Machining Technology of Ministry of Education, Tianjin 300072, China
China Coal Pingshuo Industry Coal Corporation, Shanxi 036000, China
NETL
NSTL
Trans Tech Publications Ltd