首页|Fabrication of MoSi_2 Nanocrystal by Mechanical Alloying Large Particle-sized Starting Powders
Fabrication of MoSi_2 Nanocrystal by Mechanical Alloying Large Particle-sized Starting Powders
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NETL
NSTL
Trans Tech Publications Ltd
The MoSi_2 nanocrystal was prepared by mechanical alloying (MA) large particle-sized starting powders, in which the milling time is much longer than usual MA time. It was found that the Mo-Si powder mixture mixed at stoichiometry proportion forms α-MoSi_2 and β-MoSi_2 in the MDR mode rather than pure α-MoSi_2 in the SHS mode. The grain size of MoSi_2, calculated using Scherrer's formula, is 18nm when milled for 96h, and decreases to 12nm when further milling to 144 h. This is because that the milling balls provide enough energy to refine most of the rough crystal grain. The average grain size increased to 15nm when milled for 192 h, which indicates that further expand time could not refine the crystal grain while cause the growth of a part of the crystal grain. The particle size of MoSi_2 is about 0.5μm when milled for 96 h and the agglomerating phenomenon is severe. The particle size of MoSi_2 decreases to 0.4μm and releases the agglomerating phenomenon with the milling time for 144 h.
MoSi_2nanocrystalmechanical alloying
Luo Junting
展开 >
College of Mechanical Engineering, State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, China
NETL
NSTL
Trans Tech Publications Ltd