Porous β-Ticalcium Phosphate Composite Scaffold Reinforced by K_2HPO_4 and Gelatin

扫码查看
To improve the mechanical strength of porous P-tricalcium phosphate (β-TCP) scaffold, porous β-TCP composite scaffold was prepared by immersing as-sintered porous β-TCP scaffold mixed with K_2HPO_4 in gelatin solution, following vacuum drying and glutaraldehyde cross-linking. The pattern of samples was characterized by X-ray diffraction (XRD). The surfaces of samples were analyzed by scanning electron microscopy (SEM). The compressive strength of samples was measured by universal test machine. The porosity percentage of samples was investigated by Archimedes method. The effects of time of samples incubating in simulated body fluid (SBF) on compressive strength and weight loss of samples were also studied. The results show that the compressive strength and water-retention rate of samples can be improved by the K_2HPO_4 and gelatin. The decrease rate of compressive strength and weight loss of samples is greater initially, and then slower compared with that of β-TCP scaffolds. When the samples incubate in SBF about 45d, the compressive strength and weight become increase, and finally are greater than that of β-TCP scaffold.

porous p-tricalcium phosphategelatincomposite materials

JinGou Ji、XiaoYu Yuan、ZhiNing Xia、PengPeng Liu、JiDa Chen

展开 >

College of Chemistry and Chemical Engineering, Chongqing University, Chongqing 400044, China

College of Chemistry and Chemical Engineering, Chongqing University, Chongqing 400044, China College of Bioengineering, Chongqing University, Chongqing 400044, China

2010

Key engineering materials

Key engineering materials

ISSN:1013-9826
年,卷(期):2010.434/435