首页|Preparation and Thermal Conductivity of Hf_6Ta_2O_(17) Ceramic
Preparation and Thermal Conductivity of Hf_6Ta_2O_(17) Ceramic
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NETL
NSTL
Trans Tech Publications Ltd
Hf_6Ta_2O_(17) ceramic powder was prepared by solid state reaction at 1600℃ for 10 hours. The phase and microstructure of Hf_6Ta_2O_(17) ceramics were observed. The XRD results revealed that the sintered sample of the ceramic powder had single phase and the SEM results showed that the sintered sample was comparative dense. The thermal conductivity of the sintered sample was investigated and the value was comparative low.
Hf_6Ta_2O_(17)solid state reactionthermal conductivity
M. Li、Q. Xu、L. Wang