首页|Defects Analysis of Large Size Silicon Nitride Balls Sintered by Gas Pressure Sintering
Defects Analysis of Large Size Silicon Nitride Balls Sintered by Gas Pressure Sintering
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NETL
NSTL
Trans Tech Publications Ltd
The sections of Φ55mm silicon nitride balls, sintered by gas pressure sintering were analyzed. The results show that temperature gradient during of the sintering process from the surface to the core of large size silicon nitride balls occurred because of the lower thermal conductivity of Si_3N_4. With the diameter increasing, the temperature gradient was more visible. The impurity of raw materials, such as free Si, free C and other metal oxides, like the SiO_2 could produce gas, such as SiO, CO and so on, during the sintering process through the thermodynamic analysis. The producing gas exhausted more difficultly with the diameter of silicon nitride balls increasing. These factors were the most important to the defects of large size silicon nitride balls during the sintering process and made cracks and crescent on the surface of balls.
NETL
NSTL
Trans Tech Publications Ltd