Crack Bridging in Stress Corrosion Cracking of Duplex Stainless Steels
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NETL
NSTL
Trans Tech Publications Ltd
Wedge open loaded (WOL) specimens of age hardened Zeron 100 duplex stainless steel were tested in 3.5 wt % NaCl solution with cathodic polarizes applied at-900mV/SCE to investigate stress corrosion cracking mechanism in duplex stainless steel. The interaction between microstructure and mechanism of stress corrosion cracking was studied. Fracture mechanism was studied by using scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD). The material was found cracked by ferrite cleavage, austenite tearing and austenite dissolution by environment. The ferrite cleavage took place along {100} planes and {112} twin habit planes. The austenite grains appear to act as crack bridging & crack arrester and failed by tearing & stress corrosion cracking.