首页|Synthesis and properties characterization of an Al2O3-based ceramic materials with intragranular self-lubricating nanostructure
Synthesis and properties characterization of an Al2O3-based ceramic materials with intragranular self-lubricating nanostructure
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
? 2022 Elsevier LtdIn this study, a novel intragranular self-lubricating nanostructure was proposed for preparing a potential ceramic cutting tool material. Nano-sized CaF2, which meets the requirements of such a material, was prepared and used in the synthesis of ceramic materials with intragranular self-lubricating nanostructure. Based on the obtained results, an Al2O3/TiC/CaF2 intragranular self-lubricating nanostructure ceramic material was prepared by vacuum hot-pressing sintering. As the nano-sized CaF2 content increased, the flexural strength first increased and then decreased, hardness decreased, and fracture toughness increased. The results indicated that the formation of intragranular nanostructures could significantly improve the friction performance of this material. The friction coefficient of this material against a 40Cr steel ball was 0.12–0.25, and decreased as the CaF2 content increased. The wear rate also decreased as the CaF2 content increased from 3.3–10 vol%, but the friction coefficient decreased only slightly. Furthermore, the wear rate increased when 13.3 vol% CaF2 was added.
Friction and wear propertyIntragranular self-lubricating nanostructureMechanical propertyNano-sized solid lubrication
Yi M.、Wang J.、Bai X.、Xu Y.、Xiao G.、Chen Z.、Zhang J.、Chen H.、Xu C.
展开 >
School of Mechanical and Automotive Engineering Qilu University of Technology Shandong Academy of Sciences
NSTL
Elsevier