A study on the formation of multiple intermetallic compounds of friction stir processed high entropy alloy particles reinforced Al matrix composites
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
In this paper, AlCoCrFeNi high-entropy alloy (HEA) particles was used as the reinforcement for aluminum matrix composites fabricated by friction stir processing. HEA particles were uniformly dispersed in the aluminum matrix. The formation of multiple intermetallic compounds and interface behavior were closely evaluated. The HEA-Al interface consisted of Al-13(CoCrFeNiMg)(4), Al-9(CoFeNi)(2) and Al18Cr2Mg3, and the interface formation and growth behavior were investigated by coupling the thermodynamics and kinetics factors. The low effective Gibbs free energy of Al-13(CoCrFeNiMg)(4) and Al-9(CoFeNi)(2) phases is the thermodynamic nature of their generation at the interface. Compared with as-received Al, the fabricated composites exhibited 16.8% higher yield strength and 28.1% higher tensile strength, and the elongation was retained to 15.3%. Both of brittle and ductile fracture characteristics were observed on the surface of the HEA particles.
NSTL
Elsevier