首页|Preparation of nano-scaled WC powder by low-temperature carbothermic reduction method
Preparation of nano-scaled WC powder by low-temperature carbothermic reduction method
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
Nano-scaled WC powder is an important material for preparation of ultrafine or nano-grained WC-based cemented carbides via powder sintering method. In this paper, nano-scaled WC powder was prepared based on traditional carbothermic reduction method. First, the mixture of WO3 and carbon were reacted at 1000 degrees C to remove all the oxygen atom. Then, according to residual carbon content in the deoxidation products, the gasphase (by 90%H-2 + 10%CH4, at 900 degrees C) or solid-phase carburizing process (at 1100 degrees C) was selected to prepare WC powder, respectively. The results indicated that the use of nano carbon black in first stage could provide a large number of dispersed nuclei, and meanwhile, a low reaction temperature was beneficial to inhibit the growth of product particles. The thermodynamic calculation, reaction behavior and nuclei growth behavior in deoxidation and carbonization stages were studied in detail. As the C/WO3 ratio was 2.5 and 3.8, the WC powder with total carbon content of 6.23% and 6.19%, particle size of 80.29 nm and 95.24 nm, and BET value of 3.88 m(2)/g and 4.25 m(2)/g was obtained by this method, respectively.
NSTL
Elsevier