首页|Effect of Mn addition on the formation of vacancy-type dislocation loops in α-Fe
Effect of Mn addition on the formation of vacancy-type dislocation loops in α-Fe
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
? 2022 Elsevier Inc.It has recently been established that vacancy loops of ~100 nm in maximum size could form in hydrogen pre-implanted α-Fe (Huang et al. Fusion Eng. Des., 2010). The formation temperature of these large loops is composition dependent, varying from ~500 °C in α-Fe, to ~450 °C in Fe[sbnd]Ni and ~ 620 °C in Fe[sbnd]Cr (Wan et al. J. Nucl. Mater., 2014; Du et al. Acta Metall. Sin., 2019). In this work, the effect of Mn addition upon vacancy loop formation has been investigated. Pure Fe and Fe-1.4 wt% Mn alloy specimens were irradiated with 30 keV H+ ions at room temperature. Radiation-induced loop production, size, population and nature were characterized based on diffraction contrast imaging using a combination of 1 MV high voltage electron microscope (HVEM) and 200 kV conventional transmission electron microscope (CTEM). Results of observation indicate that Mn addition gives rise to the increase of vacancy loop formation temperature in α-Fe, similar to the effect of Cr. A new criterion has been thus proposed, to classify the common alloying elements (Cr, Ni, Mn etc) found in Fe.
Fe[sbnd]Mn alloyHigh-voltage electron microscopeHydrogenVacancy loop
Li R.、Yi X.、Han W.、Liu P.、Zhan Q.、Wan F.、Xue L.、Watanabe H.
展开 >
School of Materials Science and Engineering University of Science and Technology Beijing
Research Institute for Applied Mechanics Kyushu University
NSTL
Elsevier