Post-irradiation examination of U-7Mo/Mg and U-10Mo/Mg dispersion fuels irradiated in the NRU reactor
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
As part of a global initiative to reduce the usage of highly enriched uranium (HEU) fuel for research and test reactors, Al-clad U-7Mo/Mg and U-10Mo/Mg pin-type mini-elements with a low-enriched uranium (U-235 enrichment of 19.75 wt%) loading of 4.5 g U/cm3 were fabricated at the Canadian Nuclear Laboratories (CNL). The mini-elements were irradiated in the National Research Universal (NRU) reactor at maximum linear power ratings of 100 kW/m up to 80 at% U-235 burnup. Hot cell macroscopic examination of the discharged fuel elements at 30, 60 and 80 at% U-235 burnup indicated that they were intact without breakaway swelling or fuel cladding failure. The results of interim post-irradiation examination (PIE) that was conducted on mini-elements discharged at 30 at% U-235 burnup are reported in this paper. A follow-up paper will present the PIE results of the mini-elements that achieved burnups of 60 and 80 at% U-235. In the present study, the microstructure and phase composition of the irradiated U-7Mo/Mg and U-10Mo/Mg fuel cores were investigated using optical microscopy and neutron diffraction analysis. The weight fraction of different crystalline phases in U-7Mo/Mg and U-10Mo/Mg fuel cores at low burnup was determined through Rietveld refinement. This paper includes a description of the irradiation tests along with preliminary PIE results from the irradiated U-Mo/Mg mini-elements and describes the results of optical microscopy characterization and neutron diffraction analysis.
NSTL
Elsevier