首页|Unexpected failure of cast superduplex stainless steel exposed to high chlorides containing water: From failure analysis to corrosion mechanisms settlement
Unexpected failure of cast superduplex stainless steel exposed to high chlorides containing water: From failure analysis to corrosion mechanisms settlement
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
? 2022 Elsevier LtdThis work deals with the failure analysis of a super duplex valve operating in technical waters with high chlorides content up to 80 °C. A careful fracture surfaces and microstructural characterization was combined with corrosion studies (SKPFM (Scanning Kelvin Probe Force Measurements) and polarization curves) of different valve regions in order to determine the failure mechanism. It was found that the cast material presents a segregated microstructure containing ferritic phases with different PREN (Pitting Resistance Equivalent Number). This strongly affects the corrosion properties of the material, enhancing the susceptibility to localized corrosion and leading to SCC (Stress Corrosion Cracking) failure.
Pitting corrosionScanning Kelvin Probe analysisStress corrosionSuperduplex stainless steelWeight loss
Lanzutti A.、Andreatta F.、Magnan M.、Fedrizzi L.、Gerolin A.
展开 >
University of Udine Polytechnic Department of Engineering and Architecture
NSTL
Elsevier