首页|Selective etching of in-situ formed La2O3 particles to prepare porous LaCoO3 perovskite for catalytic combustion of ethyl acetate
Selective etching of in-situ formed La2O3 particles to prepare porous LaCoO3 perovskite for catalytic combustion of ethyl acetate
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
A selective etching method was reported to prepare porous LaCoO3 perovskite for catalytic combustion of ethyl acetate (EA). The porous LaCoO3 was obtained by selectively etching of in-situ formed La2O3 particles with acetic acid (HAc) from a pre-synthesized LaCoO3-La2O3 composite. XRD, N-2 physisorption, ICP-OES, TEM, XPS, H-2-TPR and O-2-TPO showed that the etching of La2O3 with HAc not only generated surface La defects, but also improved the porosity, the exposure of active sites and the redox properties of the material. Therefore, the porous LaCoO3 can contact and activate the reactants efficiently, accelerating the reaction rate. LCO2.0-30, prepared with La/Co molar ratio of 2.0 and etched for 30 min, was the most active catalyst even in presence of H2O, with 100% EA conversion at 220 degrees C, due to its abundant porosity, surface active sites and strong reducibility. A possible reaction mechanism for EA combustion conducted on porous LaCoO3 perovskite was proposed.
Selective etchingIn-situ formed La2O3Porous LaCoO3Catalytic combustionEthyl acetateReaction mechanismCO OXIDATIONLA-COOXIDESPERFORMANCESTOLUENESOOTSILICALAMNO3MNCE
Wang, Shan、Zhu, Junjiang、Carabineiro, Sonia A. C.、Xiao, Ping、Zhu, Yujun
NSTL
Elsevier