首页|Corrosion crack failure analysis of 316L hydraulic control pipeline in high temperature aerobic steam environment of heavy oil thermal recovery well
Corrosion crack failure analysis of 316L hydraulic control pipeline in high temperature aerobic steam environment of heavy oil thermal recovery well
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
? 2022The 316L hydraulic control pipeline (HCP) easily caused corrosion failure in the process of heavy oil recovery. In this study, the corrosion failure of 316L HCP in the 260–350 °C high temperature aerobic steam environment was investigated by using autoclave. Based on SEM, EDS, cracks morphology and XPS analysis, the failure mechanism of 316L HCP exposure in different high temperature steam environments was concluded. The results indicate that the corrosion fracture occurs at 260 °C. The SCC cracking was transgranular propagation, and the corrosion failure was attributed to anodic dissolution stress corrosion cracking. With the increase of temperature, the formation of absorbed water film on the surface contributes to improving the compactness of corrosion products which could prevent the crack propagating under corrosion medium. Moreover, the high temperature significantly affected the content of Cr(OH)3 and Ni(OH)2 in the oxide film which improved the corrosion resistance of stainless steel.
316L hydraulic control pipelineCorrosion failureHigh temperature aerobic steam environmentStress corrosion cracking
Ma Z.、Wang T.、Li H.、Liu W.、Chen L.、Fan P.、Dong B.
展开 >
Oil Production Division China Oilfield Service Limited
Corrosion and Protection Center Institute for Advanced Materials and Technology University of Science and Technology Beijing
NSTL
Elsevier