Corrosion behavior and surface characterization of an equiatomic CoCrFeMoNi high-entropy alloy under various pH conditions
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
The corrosion behavior and surface characterization of an equiatomic CoCrFeMoNi high-entropy alloy (HEA) under various pH conditions were investigated by Mott–Schottky measurements, EIS, polarization, and XPS. The results showed that the passive films formed on the HEA displayed the n–p heterojunction electronic structure due to the generation of different semiconducting constituents. As the pH increased, the donor density decreased, which was attributed to the acceleration in the annihilation rate of the oxygen vacancies. Cr and Mo species were stable and were found enriched in the passive films, while substances of Co, Fe and Ni were depleted, independent of pH. Co and Ni mainly existed in the films in their metallic forms, both of which contributed less to the passive film formation. The stability of Fe was markedly enhanced with the pH increasing, resulting in the main components of the passive films changing from Cr and Mo to Cr, Fe and Mo.
HEAMott–SchottkyPassive filmpHXPS
Wang Z.、Zhang G.-H.、Jin J.、Zhang L.、Du Y.-X.、Fan X.-H.
展开 >
Institute for Advanced Materials and Technology University of Science and Technology Beijing
China Petroleum Engineering & Construction Corp. Beijing
NSTL
Elsevier