Achieving higher dynamic mechanical response by adjusting texture through twinning in a ZK61 Mg alloy
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
In this study, texture c-axis//ND of ZK61-T6 Mg alloy was reoriented towards c-axis//ED, TD and tilted in between ED and TD in a ZK61-PC Mg alloy through cross pre-compression. Subsequently, quasi-static and dynamic mechanical behaviour was examined. The results showed that compressive yield strength, ultimate compressive strength and elongation to fracture were considerably increased from 140 to 220 MPa, 374–437 MPa and 0.15–0.16, respectively. This increase was the synergistic effect of texture, grain refinement through twin boundaries and pre-induced dislocation hardening effect. In addition, an exceptional increase of ultimate compressive strength (531 MPa) was obtained under dynamic loading. The microstructure evolution of deformed specimens revealed that the propensity and width of the adiabatic shear band were increased with an increase in strain rate in ZK61-PC Mg alloy. In addition, twinning, de-twinning,<a> and<c+a> dislocation inside the twin and the matrix absorbed the high-stress energy and provided a higher mechanical response in ZK61-PC Mg alloy. The twinning induce rotational dynamic recrystallization mechanism was responsible for the development of fine grains. Based on the results, it is recommended that pre-compression is a practical way to increase the efficiency of the ZK61 Mg alloy.
NSTL
Elsevier