Failure analysis of anion synergy on pitting behavior of liner 316L in sour water system by electrochemical tests
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
Electrochemical tests were employed to study the chloride, sulfate and carbonate ions synergistically effects on pitting. The results showed that SO42- increased the pitting potential of 316L at first and then decreased, peaking at 0.2 M. In this case, the highest critical pitting temperature (12 degrees C), the breakdown potential (0.45 V-SCE), and the maximum impedance (257 k Omega cm(2)) were obtained. The existing CO32- raised the pitting potential but accelerated the general corrosion of 316L surface. The effective adsorption area based on the competitive adsorption mechanism of the anions was proposed to interpret the pitting and the passivation behaviors of 316L, and the properties of the passive film were comprehensive analyzed.