首页|Interface stability and fracture mechanism of Al/Steel friction stir lap joints by novel designed tool
Interface stability and fracture mechanism of Al/Steel friction stir lap joints by novel designed tool
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
A novel welding tool, characterized by the enlarged pin design was developed to solve the hook feature or insufficient interface deformation for Al/steel friction stir lap welded joints. The welding tool enhanced the interface deformation effect and eliminated hook feature. The thickness of the intermetallic compound (IMC) layer at the interface decreased from 3.3 mu m to 0.46 mu m, when the welding speed increased from 30 mm/min to 300 mm/min. The laminated structure composed of IMCs and fine steel grains gradually disappeared, with the interface gradually changing from serrated to straight as welding speed increased. The nanohardness value of the microstructure reached 9.4 +/- 0.3 GPa at a distance of 10 mu m from the interface layer. Due to the larger metallurgical bonding area, the best line load 499.4 N/mm reached 52 % of the 3 mm 6082-T6 alloy, which was obtained at the rotational speed of 1200 r/min and the welding speed of 50 mm/min. Four different interface failure modes were found and established during the shearing process. The strain concentration phenomenon of the successive occurrence, development and transfer of interface failure presented obvious interval character-istics in time and space.
Al/steelFriction stir lap weldingNovel tool designInterface formationMechanical propertiesFracture mechanismALUMINUM-ALLOYALMICROSTRUCTUREZN
Liu, Jinglin、Hao, Zilin、Xie, Yuming、Meng, Xiangchen、Huang, Yongxian、Wan, Long