Hot corrosion behavior of a NiCoCrAlY coating fabricated by laser cladding on 17-4PH stainless steel
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
NiCoCrAlY coatings were prepared using laser cladding technology and subjected to a continuous hot corrosion test in a eutectic Na2SO4/NaCl (75:25, wt. %/wt. %) salt at 800 degrees C in air. The corrosion kinetics curves of the NiCoCrAlY coating and the untreated substrate over 100 h of hot corrosion were compared and analyzed. The results show that in the early stage of hot corrosion, a chemical reaction that produces alkaline fusion near the oxide scale takes place at the molten salt/coating interface, causing Al2O3/Cr2O3 to form and dissolve continuously. In the late stage, a new continuous Al2O3 film is formed.