首页|Correlation between dynamic magnetization process and dynamic domains of high saturation induction FeSiBNbCuMo nanocrystalline alloy with dual anisotropies
Correlation between dynamic magnetization process and dynamic domains of high saturation induction FeSiBNbCuMo nanocrystalline alloy with dual anisotropies
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
Improving the high-frequency properties of the relatively high saturation induction alloys is significance for widening the frequency range of the noise suppression of common mode chokes. Herein, transverse magnetic field annealing after having been nano-crystallized (TA) was performed to the as-quenched Fe76Si13B8Nb1.5Cu1Mo0.5 alloy, and the dynamic properties, microstructure, and dynamic domains were in detail studied comparing with those annealed without magnetic field (NA). It was found that TA at 400 °C caused an increase in permeability at 50 kHz by 41% and a decrease in core loss at 0.2 T and 50 kHz by 30%, in comparison with those of NA. TA at 400 °C induced the ratio of field induced anisotropy constant Ku to average random anisotropy constant<K1> to be ~ 1.3 and inhomogeneous rotation, leading to the promoted domain refinement with increasing frequency and improved high-frequency properties, compared with that of NA bears only<K1> ~5.4 J/m3. Moreover, the role of dual anisotropies on the magnetic domain structures, dynamic magnetization process and magnetic performances were obtained and its correlation model based on the experimental results was established. These results could provide a good guide for performance optimization to meet higher frequency requirements of common mode chokes application.
Magnetic anisotropyMagnetic domain structureMagnetic performanceMagnetization processNanocrystalline alloy
Zhang B.、Liu Y.、Zhang R.、Zhang J.、He A.、Xie L.、Dong Y.、Li J.
展开 >
CAS Key Laboratory of Magnetic Materials and Devices Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology Ningbo Institute of Materials Technology and Engineering Chinese Academy of Sciences
Taiyuan University of Technology Taiyuan Univ Technol Coll Elect & Power Engn Natl & Prov Joint Engn Lab Min Intelligent Elect Shanxi Key Lab Coal Min Equipment & Safety Contro
NSTL
Elsevier