? 2022NiAlY alloys with the addition of Zr, Ti, Ta and Mo were prepared by arc melting. The oxidation and NaCl-induced hot corrosion behavior of the alloys were investigated at 650 ℃, with the focus on the effect of element-doping and phase. With the addition of Ti, Ta and Mo, the oxidation resistance of the tested alloys was effectively enhanced compared to the undoped NiAlY alloy. However, the NiZrAlY alloy showed very poor oxidation resistance. Under the NaCl-induced hot corrosion test, the NiTaAlY and NiMoAlY alloys exhibited an improved hot corrosion resistance, while the NiZrAlY and NiTiAlY alloys showed very poor hot corrosion resistance. Moreover, the NiAl and Ni5Y phases exhibited different behavior during the oxidation and NaCl-induced hot corrosion tests.