首页|Mechanical and magnetic properties of (Ti,W)C-xCoCrFeNiMo cermets sintered at different sintering temperatures
Mechanical and magnetic properties of (Ti,W)C-xCoCrFeNiMo cermets sintered at different sintering temperatures
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
NSTL
Elsevier
This work aims to explore the effects of different sintering temperatures on microstructure, mechanical properties and magnetic properties of (Ti,W)C-xCoCrFeNiMo (wt%, x = 15, 30) cermets. Results showed that bending strength, hardness and fracture toughness of sintered cermets first increased and then decreased with the increase of sintering temperature. They reached peak values of about 967.2 MPa, 92.8 HRA and 9.1 MPa.m(1/2) for x = 15, and 1278.3 MPa, 91.2 HRA and 13.6 MPa.m(1/2) for x = 30, after sintering at 1450 ?, respectively. The Ms, Mr, and chi(max) of cermets first increased, then decreased and finally increased. They reached minimum to 1.08 emu/g, 0.09 emu/g and 6.58 emu/(g.KOe) for x = 15 at 1450 ? and 1.18 emu/g, 0.02 emu/g and 8.49 emu/ (g.KOe) for x = 30 at 1410 ?, respectively. This was related to the higher content of non-ferromagnetic elements and the weak magnetic phase Ni3Mo3C in the binder phase
NSTL
Elsevier