Effect of B2O3 doping on structure and properties of 0.76BF-0.24BT high temperature lead-free piezoelectric ceramics
In order to study the effect of doping B2O3 on ceramics,0.76BiFeO3-0.24BaTiO3-xB2O3(0.76BF-0.24BT-xBO)high tem-perature lead-free piezoelectric ceramics were prepared by solid phase synthesis method,x is the mole fraction.The effects of differ-ent BO content on phase structure,microstructure,electrical properties,Curie temperature and depolarization temperature of ceram-ics were studied.XRD analysis show that all samples are of rhomb tripartite perovskite structure.The observation of microstructure shows that the grain distribution is uniform,and there is liquid phase between grain boundaries,and the grain size increases with the increase of x.The optimal sintering temperature of ceramics was reduced from 960 ℃ to 940 ℃.When x=0.1,the excellent electri-cal properties are obtained:d33=101 pC·N-1,Pr=21.5 μC cm-2.0.76BF-0.24BT-xBO ceramics have good high temperature stability:TC=585 ℃,Td=560 ℃.The results show that the doping of B2O3 can improve the microstructure,reduce the sintering temperature and improve the electrical properties of 0.76BF-0.24BT ceramics.
万方数据