固溶处理对粉末注射成形高氮无镍不锈钢组织和性能的影响

扫码查看

原文链接

NETL
NSTL
万方数据

中文摘要：为了提高粉末注射成形技术制备的高氮无镍奥氏体不锈钢的性能,开展了后续固溶热处理.系统研究了固溶温度、固溶保温时间对不锈钢微观组织和力学性能的影响,并对固溶前后不锈钢样品的耐腐蚀性能进行了比较.结果显示:渗氮烧结后奥氏体基体中析出的Cr2N第二相影响了不锈钢的力学和耐腐蚀性能.固溶处理后,烧结形成的Cr2N第二相消失,为纯奥氏体组织.当固溶温度为1 150 ℃,固溶保温时间为10 min时,不锈钢抗拉强度达到889 MPa,延伸率达到16.8％,力学性能最优.与固溶处理前相比,固溶处理后不锈钢样品腐蚀评级由0级提高到10级,耐腐蚀性能大幅提高.

外文标题：Effects of solution treatment on the microstructures and properties of high nitrogen nickel-free stainless steel prepared by MIM

外文摘要：In this study,subsequent solution heat treatment was carried out in order to improve the prop-erties of high nitrogen nickel-free austenitic(HNNFA)stainless steel prepared by MIM.The effects of solution temperature and duration on the microstructures and mechanical properties of HNNFA stain-less steel were systematically studied.In addition,the corrosion resistances of stainless steel specimens before and after solution treatment were compared.The results show that Cr2N precipitates in the aus-tenitic matrix after sintering,thus affecting the mechanical and corrosion resistance of the HNNFA stainless steel.The secondary phase of Cr2N disappears after solution heat treatment and the microstruc-ture is composed of pure austenite.When the solution temperature is 1150 ℃ and the holding time is 10 min,the HNNFA stainless steel has the best mechanical properties.Its tensile strength reaches 889 MPa and elongation reaches 16.8％.Compared with the specimens before solid solution treatment,the corrosion rating of HNNFA stainless steel after solution treatment is increased from 0 to 10,and the corrosion res-istance is greatly improved.

外文关键词：

high nitrogen nickel-free stainless steelmetal injection moldingsolution treatmentnitridemechanical propertiescorrosion resistance

作者：

邹黎明、刘瑞洋、蔡瑛、倪东惠

展开 >

作者单位：

广州科技贸易职业学院智能制造学院,广东广州 511442

鞍钢房产建设集团有限公司,辽宁鞍山 114000

广州金南磁性材料有限公司,广东广州 511328

华南理工大学机械与汽车工程学院,广东广州 510641

展开 >

关键词：

高氮无镍不锈钢粉末注射成形固溶处理氮化物力学性能耐腐蚀性能

基金：

广州市教育局羊城学者科研专项广东省教育厅特色创新科研专项广州市基础与应用基础研究专项广州市增城区创新领军团队专项

项目编号：

2022353792021KTSCX273202201011608202102004

出版年：

2024

DOI：

10.7513/j.issn.1004-7638.2024.04.019

钢铁钒钛

攀钢集团攀枝花钢铁研究院有限公司

钢铁钒钛

CSTPCD北大核心

影响因子：0.395

ISSN：1004-7638

年,卷(期)：2024.45(4)