TP347H不锈钢与BT700-l合金的应力腐蚀行为
Stress corrosion behavior of TP347H stainless steel and BT700-1 alloy
李冬升 1刘仁才 1涂宇航 1兰轲钰1
作者信息
- 1. 江苏大学材料科学与工程学院,江苏 镇江 212013
- 折叠
摘要
利用慢应变速率拉伸(SSRT)应力腐蚀试验,对高盐腐蚀环境下TP347H不锈钢与BT700-l合金的应力腐蚀开裂(SCC)行为进行了研究.结果表明:在不同pH值高盐溶液中TP347H不锈钢与BT700-l合金均未发生SCC行为;仅在酸性腐蚀环境中由于Cl-致敏和H+催化促进下致使TP347H不锈钢与BT700-l合金表现出一定的SCC倾向,断口呈现韧-脆混合开裂特征;在酸性腐蚀环境中,BT700-l合金的抗应力腐蚀性能明显高于TP347H不锈钢.
Abstract
Stress corrosion cracking(SCC)behavior of TP347H stainless steel and BT700-l alloy in high concentration salt corrosion environment was studied by using slow strain rate tensile(SSRT)stress corrosion test.The results show that there is no SCC behavior between the TP347H stainless steel and BT700-l alloy in high concentration salt solution with different pH values.The TP347H stainless steel and BT700-l alloy show a certain SCC tendency under the condition of Cl-sensitization and H+catalysis in acidic corrosion environment,and the fractures are tough-brittle mixed cracking.The stress corrosion resistance of the BT700-l alloy in acid corrosion environment is significantly higher than that of the TP347H stainless steel.
关键词
TP347H不锈钢/BT700-l合金/慢应变速率拉伸/应力腐蚀(SCC)/高盐溶液Key words
TP347H stainless steel/BT700-l alloy/slow strain rate tensile(SSRT)/stress corrosion cracking(SCC)/high concentration salt solution引用本文复制引用