首页|Analysis of deformation mechanisms in magnesium single crystals using a dedicated four-point bending tester

Analysis of deformation mechanisms in magnesium single crystals using a dedicated four-point bending tester

扫码查看
原文链接
  • NETL
  • NSTL
  • 万方数据
In this study,we explored the deformation mechanisms of Mg single crystals using a combination of scanning electron microscopy and elec-tron backscattered diffraction in conjunction with a dedicated four-point bending tester.We prepared two single-crystal samples,oriented along the<(11)20>and<10(1)0>directions,to assess the mechanisms of deformation when the initial basal slip was suppressed.In the<(11)20>sample,the primary {10(1)2 } twin(T1)was confirmed along the<(11)20>direction of the sample on the compression side with an increase in bending stress.In the<10(1)0>sample,T1 and the secondary twin(T2)were confirmed to be along the<(11)20>direction,with an orientation of±60° with respect to the bending stress direction,and their direction matched with(0001)in T1 and T2.This result implies that crystallographically,the basal slip occurs readily.In addition,the<10(1)0>sample showed the double twin in T1 on the compression side and the tertiary twin along the<10(1)0>direction on the tension side.These results demonstrated that the maximum bending stress and displacement changed significantly under the bend loading because the deformation mechanisms were different for these single crystals.Therefore,the correlation between bending behavior and twin orientation was determined,which would be helpful for optimizing the bending properties of Mg-based materials.

Four-point bendingMagnesium single crystalTwinningBasal slipScanning electron microscopyElectron backscatter diffraction

Yutaka Yoshida、Rikuto Izawa、Kenji Ohkubo

展开 >

Faculty of Engineering,Kitami Institute of Technology,Koen-cho,Kitami,Hokkaido 090-8507,Japan

Graduate student,Department of Mechanical and Electrical Engineering,Kitami Institute of Technology,Koen-cho,Kitami,Hokkaido 090-8507,Japan

Kyokuto Kaihatsu Kogyo Co.,Ltd,Awaji,Chuohu,Oosaka,Oosaka 541-0047,Japan

Center for Advanced Research of Materials,Faculty of Engineering,Hokkaido University,Kita-ku,Sappro,Hokkaido 060-8628,Japan

展开 >

AMADA FOUNDATIONJSPS KAKENHIJSPS KAKENHI

AF-2022030-B3JP16K05961JP19K04065

2024

10.1016/j.jma.2024.05.002

镁合金学报(英文)

镁合金学报(英文)

EI
ISSN：2213-9567
年,卷(期)：2024.12(5)