首页|Strength and elastic modulus enhancement in Mg-Li-Al matrix composites reinforced by ex situ TiB2 particles via stir casting
Strength and elastic modulus enhancement in Mg-Li-Al matrix composites reinforced by ex situ TiB2 particles via stir casting
扫码查看
点击上方二维码区域，可以放大扫码查看
原文链接
维普
万方数据
A novel Mg-10Li-3AI(wt.％,LA103)matrix composite reinforced by ex situ micron TiB2 particles was developed in the present study.The ball milling and cold pressing pretreatment of the reinforcements made it feasible to prepare this material under stir casting conditions with good dispersion.The microstructure and mechanical properties of the composites prepared by different pretreatment methods were analyzed in detail.The TiB2 particles in the Al-TiB2/LA103 composite using the pretreatment process were uniformly distributed in the microstructure due to the formation of highly wettable core-shell units in the melt.Compared with the matrix alloys,the Al-TiB2/LA103 composite exhibited effective strength and elastic modulus improvements while maintaining acceptable elongation.The strengthening effect in the composites was mainly attributed to the strong grain refining effect of TiB2.This work shows a balance of high specific modulus(36.1 GPa·cm3·g-1)and elongation(8.4％)with the conventional stir casting path,which is of considerable application value.
Jiawei Sun、Dehua Ding、Wencai Liu、Guohua Wu、Hongjie Liu、Guangling Wei、Hezhou Liu
展开 >
National Engineering Research Center of Light Alloy Net Forming and State Key Laboratory of Metal Matrix Composites,School of Materials Science and Engineering,Shanghai Jiao Tong University,Shanghai 200240,China
维普
万方数据