铝矾土和白云石制备高孔隙率多孔陶瓷膜
Preparation of High Porosity Ceramic Membranes from Bauxite and Dolomite
吴文秀 1李岭领2
作者信息
- 1. 广东石油化工学院 材料科学与工程学院,广东 茂名 525000
- 2. 广东石油化工学院 化学工程学院,广东 茂名 525000
- 折叠
摘要
以铝矾土和白云石为原材料,采用原位烧结来制备多孔陶瓷膜.系统研究了烧结温度与不同含量的白云石对陶瓷膜的相组成、孔隙率、收缩率、孔径分布、微观形貌和气体通量的影响.结果表明,添加白云石的陶瓷膜主要晶相是刚玉、钙长石和尖晶石.白云石的添加,抑制了铝矾土的致密化,提高了陶瓷膜的孔隙率和孔径,从而提高其气体通量,并且白云石含量越高,由温度升高所引起的孔隙率下降幅度和收缩率上升幅度越小.
Abstract
Porous ceramic membrane was prepared by in-situ sintering with bauxite and dolomite as raw materials.The effects of sintering temperature and different content of dolomite on the phase composition,porosity,shrinkage,pore size distribution,micro-morphology and gas flux of ceramic membrane were systematically studied.The results show that the main crystalline phases of the ceramic membrane with dolomite are corundum,anorthite and spinel.The addition of dolomite inhibits the densification of bauxite and increases the porosity and pore size of ceramic membrane,thus increasing its gas flux.And the higher the dolomite content is,the smaller the porosity decreases,and shrinkage increases caused by temperature increase.
关键词
白云石/铝矾土/高孔隙率/多孔陶瓷膜Key words
dolomite/bauxite/high porosity/porous ceramic membrane引用本文复制引用
基金项目
广东省基础与应用基础研究基金项目(2022A1515011927)
广东省普通高校特色创新项目(2020KTSCX082)
广东省普通高校特色创新项目(2022KQNCX049)
茂名市科技计划项目(2021016)
茂名市科技计划项目(2022029)
茂名绿色化工研究院"应用创新"项目(MMGCIRI-2022YFJH-Y-027)
大学生创新创业项目(73322020)
大学生创新创业项目(73322186)
出版年
2024
国家科技期刊平台
NSTL
万方数据