20Mn2钢链条断裂原因分析
Cause for 20Mn2 Steel Chain Breaking
王少聪 1王会强 1崔建英 2赵建新 3闫学兰 4孙玉林 5孙广军 6王晓丽7
作者信息
- 1. 河北农业大学机电工程学院,河北 保定 071001
- 2. 巨力索具股份有限公司,河北 保定 072550
- 3. 保定市东利机械制造股份有限公司,河北 保定 071100
- 4. 保定金阳光能源装备科技有限公司,河北 保定 071051
- 5. 河北田野节水灌溉设备有限公司,河北 保定 071100
- 6. 唐山利军机械制造有限公司,河北 保定 071100
- 7. 河北润农节水科技股份有限公司,河北 保定 071100
- 折叠
摘要
某厂20Mn2 钢链条在使用中断裂.为找出链条断裂的原因,检测了断裂链条的化学成分、硬度、显微组织和断口形貌.结果表明:链条表面脱碳严重,导致表面疲劳强度和硬度下降;心部有大量铁素体和氧化物夹杂,导致其力学性能降低.是这两个因素导致链条在使用中断裂.
Abstract
The 20Mn2 steel chain broke in service in a factory.In order to find out the cause of the its breaking,the broken chain was tested for chemical composition,hardness,microstructure and fracture pattern.The results showed that the chain exhibited seriously decarburized case and thereby decreased in fatigue strength and hardness,and that the chain had a large amount of ferrite and oxide inclusions,and thereby decreased in mechanical properties.The chain breaking in service was attributed to these two factors.
关键词
20Mn2钢/热处理/断裂/脱碳Key words
20Mn2 steel/heat treatment/breaking/decarburization引用本文复制引用