首页|低Co长寿命储氢合金MlNi4.57Co0.17Mn0.25Al0.41Y0.02退火工艺的研究

低Co长寿命储氢合金MlNi4.57Co0.17Mn0.25Al0.41Y0.02退火工艺的研究

扫码查看
原文链接
  • NETL
  • NSTL
  • 万方数据
采用真空感应熔炼法制备低Co长寿命储氢合金MlNi4.57Co0.17Mn0.25Al0.41Y0.02,进行不同的退火温度(1040、1060、1080℃)和保温 5、7、10 h的退火处理,研究了不同退火工艺对合金结构和电化学性能的影响.结果表明,退火有利于合金组分均匀,消除晶格应力;随着退火温度的升高和保温时间的增加,合金的吸放氢等温平衡压PCT逐渐升高,循环稳定性明显增强,合金的最大放电容量和高倍率放电性能有所下降,且退火温度对合金电化学性能的影响高于保温时间的影响.其中,经过 1060℃、保温 10 h退火的合金,其最大放电容量为 332.8 mA·h/g,容量保持率 80%的循环次数可达到 349 次,综合性能最优.
Study on Annealing Process of MlNi4.57Co0.17Mn0.25Al0.41Y0.02 Low Co and Long Life Hydrogen Storage Alloy
The low-Co MlNi4.57Co0.17Mn0.25Al0.41Y0.02 hydrogen storage alloys with long life were prepared using vacuum induction melting method.Annealing was carried at different temperatures(1040℃,1060℃,1080℃)and insulation for 5 h,7 h and 10 h,respectively.The effects of different annealing processes on the microstructure and electrochemical properties of the alloys were studied.The results show that annealing is beneficial to the uniformity of the alloy composition and the elimination of lattice stress.With the increase of annealing temperature and holding time,the isothermal equilibrium pressure of PCT curves for hydrogen absorption and desorption increases gradually,and the cycling stability of the alloys increases significantly.The maximum discharge capacity and high rate discharge performance of the alloys decrease,and the effect of annealing temperature on the electrochemical performance of the alloy is stronger than that of holding time.After annealing at 1060℃for 10 h,the maximum discharge capacity of the alloy is 332.8 mA·h/g,and the cycles of 80%capacity retention rate can reach 349 times.The alloy has the best overall electrochemical performance.

annealing processlow-Co and long-life hydrogen storage alloyelectrochemical performance

朱晓梅、刘治平、王永光、景永强、罗统钊、李倩、许永燕

展开 >

鄂尔多斯应用技术学院,内蒙古 鄂尔多斯 017000

内蒙古稀奥科贮氢合金有限公司,内蒙古 包头 014030

内蒙古稀土功能材料创新中心有限责任公司,内蒙古 包头 014030

退火工艺 低Co长寿命储氢合金 电化学性能

鄂尔多斯重大科技合作项目(2021)鄂尔多斯市科技计划(2021)内蒙古自治区大学生创新创业训练计划(2021)中央引导地方科技发展资金项目(2020)鄂尔多斯应用技术学院大学生校级创新项目(2020)鄂尔多斯市科技计划(2022)

2021EEDSCXQDFZ0152021YYI37-442021145320062020ZY0032202001102022YY046

2024

10.14158/j.cnki.1001-3814.20220126

热加工工艺
中国船舶重工集团公司热加工工艺研究所 中国造船工程学会船舶材料学术委员会

热加工工艺

CSTPCD北大核心
影响因子：0.55
ISSN：1001-3814
年,卷(期)：2024.53(8)