研究了MnCO3 对Mg-3wt%Al、Mg-9wt%Al镁合金晶粒的影响.采用金相显微镜对添加MnCO3 含铝铸造镁合金进行了显微组织分析.结果表明:铸造 Mg-3wt%Al 和 Mg-9wt%Al 的平均晶粒尺寸为 365 μm 和 340 μm,Mg-3wt%Al和Mg-9wt%Al合金晶粒度随着MnCO3 添加量增加而减小,添加质量分数为 1wt%的MnCO3 后晶粒尺寸分别减少到 90 μm和 55 μm.理论分析表明:合金熔体中形成MgO、Al4C3 和Al8Mn5 是理想的异质形核质点,由于形核质点的增加,晶粒尺寸明显减小.
Effect of MnCO3 on Grain Size of Aluminum-Containing Cast Mg Alloys
The effects of MnCO3 on grain of Mg-3wtAl and Mg-9wt%Al magnesium alloys were studied.The microstructure of as-cast Mg-Al alloys with MnCO3 was analyzed by metallographic microscope.The results show that the average grain size of Mg-3wt%Al and Mg-9wt%Al alloys is 365 μm and 340 μm,respectively and the average grain size of Mg-3wt%Al and Mg-9wt%Al alloys decreases with increasing MnCO3 addition.After the addition of 1wt%MnCO3,the grain size is reduced to 90 μm and 55 μm,respectively.Theoretical analysis show that MgO,Al4C3 and Al8Mn5 particles are considered as heterogeneous nucleation particles and the grain size decreases obviously due to the increase of nucleation particles.

magnesium alloysgrain refinementMnCO3

王岭、刘杨、赵一权、谢宇

展开 >

营口理工学院 辽宁省化学助剂合成与分离重点实验室,辽宁 营口 115014

海南科技职业大学 化学与材料工程学院,海南 海口 571126

中汽研汽车检验中心(天津)有限公司,天津 300300

镁合金 晶粒细化 MnCO3

国家自然科学基金辽宁省自然科学基金区域联合基金辽宁省自然科学基金区域联合基金辽宁省自然科学基金指导项目辽宁省化学助剂合成与分离重点实验室内部课题国家级大学生创新创业训练计划营口市博士双创计划营口理工学院高层次人才引进项目

512710462020-YKLH-262021-YKLH-1920180550724ZJNK2109201914435050QB-2019-10RC201902

2024

10.14158/j.cnki.1001-3814.20220753

热加工工艺
中国船舶重工集团公司热加工工艺研究所 中国造船工程学会船舶材料学术委员会

热加工工艺

CSTPCD北大核心
影响因子：0.55
ISSN：1001-3814
年,卷(期)：2024.53(9)
  • 1