非对称交叉轧制对AZ31镁合金微观组织的影响

扫码查看

原文链接

NETL
NSTL
万方数据

中文摘要：采用金相显微镜、背散射电子衍射仪(EBSD)研究了对称交叉轧制和非对称交叉轧制对AZ31 镁合金微观组织的影响.结果表明:非对称交叉轧制在晶粒细化方面明显优于对称交叉轧制.经 4 道次非对称交叉轧制退火后,AZ31 镁合金平均晶粒尺寸为 10 μm,而经 4 道次对称交叉轧制后AZ31 镁合金平均晶粒尺寸为 20 μm.与对称交叉轧制AZ31 板材相比,非对称交叉轧制AZ31 板材(0002)基面织构强度较低,且极轴偏离ND方向 20°左右.

外文标题：Influence of Asymmetric Cross-Rolling on Microstructure of AZ31 Mg Alloy

外文摘要：The effects of symmetrical-cross rolling and asymmetric-cross rolling on the microstructure of AZ31 magnesium alloy were studied by optical microscope and EBSD.The results show that asymmetric-cross rolling is superior to symmetric-cross rolling in grain refinement.The average grain size of AZ31 magnesium alloy is 10 μm after four passes of asymmetric-cross rolling and annealing,while the average grain size of AZ31 magnesium alloy after 4 passes of symmetrical cross rolling is 20 μm.Compared with that of the symmetric-cross rolled AZ31 plate,the(0002)basal texture strength of the asymmetri-cross rolled AZ31 plate is lower and the polar axis is deviated about 20°from ND direction.

外文关键词：

AZ31 magnesium alloyasymmetric-cross rollingmicrostructure

作者：

王岭、赵一权、王轶农、李璞

展开 >

作者单位：

营口理工学院辽宁省化学助剂合成与分离重点实验室,辽宁营口 115014

海南科技职业大学化学与材料工程学院,海南海口 330044

中汽研汽车检验中心(天津)有限公司,天津 300300

大连理工大学材料科学与工程学院,辽宁大连 116024

国合通用测试评价认证股份公司,北京 101140

展开 >

关键词：

AZ31镁合金非对称交叉轧制微观组织

基金：

国家自然科学基金项目辽宁省自然科学基金区域联合基金项目辽宁省自然科学基金区域联合基金项目辽宁省自然科学基金指导计划项目辽宁省化学助剂合成与分离重点实验室内部课题全国大学生创新创业计划项目营口市博士双创计划项目营口理工学院优秀科技人才支持计划资助项目

项目编号：

512710462020-YKLH-262021-YKLH-1920180550724ZJNK2109201914435050QB-2019-10RC201902

出版年：

2024

DOI：

10.14158/j.cnki.1001-3814.20220557

热加工工艺

中国船舶重工集团公司热加工工艺研究所中国造船工程学会船舶材料学术委员会

热加工工艺

CSTPCD北大核心

影响因子：0.55

ISSN：1001-3814

年,卷(期)：2024.53(13)