掺加SiO2的SBS改性沥青抗紫外老化提升技术

Improvement Technology for UV Aging Resistance of SBS Modified Asphalt Mixed With SiO2

苟天波 ¹刘自金 ¹龙坤 ²毛成³

扫码查看

作者信息

1. 四川省交通建设集团有限责任公司,四川成都 610041
2. 西南交通大学土木工程学院,四川成都 610031;道路工程四川省重点实验室,四川成都 610031
3. 四川交投设计咨询研究院有限责任公司,四川成都 610041
折叠

摘要

为了提高沥青的抗紫外老化性能,使用成本较低的SiO2作为抗紫外老化改性剂对SBS沥青进行改性.通过研究SBS改性沥青在紫外老化前后表面张力、流变性能和化学成分的变化,评估了 SiO2及其掺量对SBS改性沥青抗紫外老化性能的影响.研究结果表明:SiO2与SBS改性沥青仅发生物理混合,掺加SiO2能够提高SBS改性沥青的抗紫外老化性能,当其掺量为0.8％时,制备的SBS改性沥青具有优异的高温抗变形能力、抗疲劳性能、低温抗裂性能和抗水损害性能.

Abstract

In order to improve the anti UV aging performance of asphalt,low-cost SiO2 was used as an anti UV aging modifier to modify SBS asphalt.The influence of SiO2 and its dosage on the UV aging resistance of SBS modified as-phalt was evaluated by studying the changes in surface tension,rheological properties and chemical composition be-fore and after UV aging.The research results indicate that SiO2 and SBS modified asphalt only have physical mixing.The addition of SiO2 can improve the UV aging resistance of SBS modified asphalt.When the dosage is 0.8％,the prepared SBS modified asphalt has excellent high-temperature deformation resistance,fatigue resistance,low-tem-perature crack resistance,and water damage resistance.

关键词

SBS改性沥青/SiO2/紫外老化/性能提升

Key words

SBS modified asphalt/SiO2/UV aging/performance improvement