There is an urgent need to develop low-cost,high-strength,and toughness grades of steel for domestic wind power fasteners in order to enhance the competitiveness of the industrial chain and fully participate in market competition.Through the control of smelting process to assure residual w[P]≤0.015% and w[S]≤0.010% and the total oxygen content w[T.O]stably controlled to be less than 10×10-6 during low oxygen operation practice.Two stage low-temperature rolling is adopted and the single pass reduction rate is controlled between 8% to 12% .A 10.9-grade 32CrB4 bolt steel with good impact toughness at-40℃low-temperature for ϕ38.8 mm specification has been successfully developed.The results of mechanical property inspection and metallographic observation indicate that the developed steel has good tensile properties and excellent low-temperature impact properties.The optimal heat treatment process has been studied,which is 820℃soaking water quenching and 510℃soaking tempering.The room temperature tensile strength can reach 1 075 MPa,and the average low-temperature impact value of-40℃KV2 can be 53 J.The microstructure is mainly tempered martensite,with excellent and comprehensive mechanical properties and good uniformity.
关键词
紧固件用钢/热轧棒材/热处理工艺/低温冲击/32CrB4钢
Key words
Steel for Fasteners/Hot Rolled Bars/Heat Treatment Process/Low-temperature Impact/32CrB4 Steel
维普
万方数据