摘要
为实现超双疏棉织物的高效制备,将全氟癸基三甲氧基硅烷(PFDMS)与氨水和无水乙醇(EtOH)复配水解,通过一步浸渍法制备了耐久超双疏棉织物.采用扫描电子显微镜、X射线光电子能谱仪对织物的表面形貌及元素组成进行分析,探讨了PFDMS用量及水解时间对织物表面润湿性的影响,测试了织物表面超双疏涂层的稳定性、耐久性和自清洁性能.结果表明:当PFDMS与EtOH的体积比为 3∶50 时,不同水解时间整理的棉织物均具有超双疏特性,水解 10 min时整理棉织物的水接触角高达 157.2°±0.3°,油接触角为150.0°±1.4°;PFDMS整理后的棉织物表面引入了 CF2、CF3 基团,F、Si元素的含量分别为0.66%和3.37%;整理棉织物经 10000 次循环磨擦、600 min超声波洗涤、24 h紫外光老化、24 h酸碱溶液或有机溶剂浸泡后,仍然具有超疏水和疏油特性.该方法及工艺简单高效,所制备的超双疏棉织物在自清洁领域具有潜在的应用前景和价值.
Abstract
With the development of economics and the improvement of living standards,people have more and more requirements for the functionality of cotton fabrics.The preparation of superamphiphobic cotton fabrics with self-cleaning,UV irradiation stability,and antifouling has attracted extensive attention in recent years.Currently,superhydrophobic/superoleophobic cotton fabrics are commonly prepared by pre-constructing micro/nano-rough structures on the surface of cotton fabrics and then modified with low surface energy by fluorinated compounds.However,the preparation methods for superamphiphobic cotton fabrics mostly have the shortcomings for complex processes and relatively long term.Therefore,it is of great significance to explore simple and efficient processes for preparing durable superamphiphobic cotton fabrics.Cotton fabrics were finished by impregnation method by using the hydrolyzed solution of perfluorodecyltrimethoxysilane(PFDMS),ammonia water,and anhydrous ethanol at the volume ratio of 1∶50∶50,1∶25∶25,3∶50∶50.The effects of the PFDMS concentrations and their hydrolyzed time on the surface amphiphobic of the fabrics were investigated.The surface morphology,elemental composition,wettability and mechanical stabilities,and chemical durability of the cotton fabrics were analyzed by scanning electron microscopy(SEM),X-ray photoelectron spectroscopy(XPS),contact angle tester,abrasion testing machine and UV aging tester.Meanwhile,the anti-fouling and self-cleaning characteristics of the superamphiphobic cotton fabrics were tested and evaluated.The results showed that the water/oil contact angle of PFDMS-coated cotton fabrics gradually increased with increasing concentration of the PFDMS solution.The cotton fabrics were finished at the volume ratio of PFDMS to ammonia and anhydrous ethanol with 3:50:50,and hydrolyzed for 10 min.It is showed superamphiphobic with a water contact angle of 157.2°±0.3° and an oil contact angle of 150.0°±1.4°.SEM and EDX analysis showed that the surface of cotton fabrics finished with PFDMS had dense rough coatings,and two additional 0.66%of F and 3.37%Si elements were found on the surface.The XPS analysis showed obvious signal peaks of Si 2s,Si 2p and F 1s,and CF2 and CF3 groups were found in the high-resolution of C 1s fit peaks.After 20 times of ultrasonic washing cycles(washing time was 600 min)for PFDMS-coated cotton fabrics,the water contact angle was 156.1°±1.3° and the oil contact angle was 147.7°±1.0°.After 10,000 times of abrasion for PFDMS-coated cotton fabrics,the water contact angle was 154.3°±0.9° and the oil contact angle was 138.4°±1.2°.After 24 h of UV aging,and 24 h of acid-base solution or organic solvent immersion,the contact angle of the surface of the superamphiphobic cotton fabric changed compared with that before the test,but the changes did not exceed 3.0°.The cotton fabric finished with PFDMS shows better self-cleaning properties and excellent anti-fouling to milk,coffee,orange juice,cola and soy sauce liquids.This process is efficient,and the prepared cotton fabric has better mechanical stability and chemical durability.The prepared durable superamphiphobic cotton fabric has the potential applications in the field of anti-fouling and self-cleaning.
基金项目
云南省农业基础研究联合专项重点项目(202101BD070001-011)
国家级大学生创新创业训练计划(202110677009)
维普
万方数据