多层瓷介电容器手工焊接质量提升
Improving the quality of manual welding of multilayer ceramic capacitor
牛润鹏 1李龙 1毛飘 1郑龙飞 1李娟 1党琳娜1
作者信息
- 1. 航空工业集团西安航空计算技术研究所,陕西 西安 710000
- 折叠
摘要
手工焊接后的多层瓷介电容器在温度循环试验过程中发生烧毁故障,故障原因为焊接过程中热应力较大导致器件本体生成裂纹.设计手工焊接试验,并经验证得出结论:在手工焊接过程中,通过降低手工焊接温度,增加焊接前印制电路板(PCB)的预热,可以避免器件本体产生裂纹;在产品设计阶段,避免选用较大尺寸封装,为PCB设计非接地焊盘,可以提高手工焊接的工艺窗口,从而提升多层瓷介电容器手工焊接质量.
Abstract
The multi-layer ceramic dielectric capacitor after manual welding was burned out in the process of temperature cycle test,and the malfunction was located in the welding process with large thermal stress causing device body cracks.It is concluded through the design and implementation of manual welding test and verification.That in the process of manual welding,the cracks in the device body can be avoided by reducing the temperature of manual welding and increasing the preheating of the printed board before welding.And in the product design stage,avoiding the selection of large size package and designing non-grounding pad for the printed board,can improve the process window of manual welding.Thus,the quality of manual welding of multi-layer ceramic dielectric vessel can be improved.
关键词
多层瓷介电容器/手工焊接/热应力/裂纹Key words
multi-layer ceramic dielectric capacitor/manual welding/thermal stress/crack引用本文复制引用
出版年
2024
NETL
NSTL
维普
万方数据