采用熔融共混法将聚(己二酸/对苯二甲酸)-丁二醇酯(PBAT)和聚(L-乳酸-衣康酸丁二醇酯)(PLBI)通过双螺杆挤出机制备了不同共混比例的薄膜，分析了不同PLBI添加量对PBAT薄膜气体透过性能及力学性能的影响，进一步结合材料的气体透过性和草莓的呼吸特性，对草莓进行气调包装(MAP)系统设计，并应用于其自发气调保鲜实验。结果表明，PLBI添加量为15%时，共混薄膜仍旧保持较好的力学性能，通过对共混比例的调控，将PBAT的CO2/O2透过比(CDP/OP)从10。57降低至3～7左右，同时提高了材料的保水性，使得该材料更适用于气调果蔬包装，应用于草莓自发气调保鲜实验，低温储藏下将草莓的货架期延长至21d。
Properties and applications of poly(butylene adipate-co-terephthalate)-based self-regulating gas film
A type of blending films based on poly(butylene adipate-co-terephthalate)(PBAT)and poly(lactic-co-butane-diol itaconate)(PLBI)were prepared at different mass ratios through melt extrusion using a twin-screw extruder.The ef-fect of PLBI content on the thermal performance,mechanical properties,and gas permeability of the blending films was investigated.The modified atmosphere packaging(MAP)system was designed on the basis of the gas permeability of material and the respiratory characteristics of strawberry.This MAP system was used for a strawberry-preserving experi-ment.The results indicated that the blended films achieved favorable mechanical properties at a PLBI content of 15 wt% .Through adjusting the blending ratio,the CO2/O2 penetration ratio of the blending films was reduced from 10.57 to about 3～7.Simultaneously,the water retention capacity of the blending films was enhanced.This makes the blend-ing films more suitable for air-adjusted fruit and vegetable packaging.This packaging system can be used to extend the shelf life of strawberries up to 21 days under low-temperature storage conditions.

poly(butylene adipate terephthalate)poly(lactic-butanediol itaconate)modified atmosphere storagemechanical propertyshelf life

周紫怡、王洋样、孙滔、蒋伟、董同力嘎、云雪艳

展开 >

内蒙古农业大学食品科学与工程学院,呼和浩特 010020

呼和浩特市回民区疾病预防控制中心,呼和浩特 010030

聚(己二酸/对苯二甲酸)-丁二醇酯 聚(L-乳酸-衣康酸丁二醇酯) 自发气调 力学性能 货架期

国家自然科学基金国家自然科学基金内蒙古自治区草原英才工程青年创新创业人才项目(2020)内蒙古农业大学杰出优秀青年科学基金

52163012219650262017XQG-4

2024

10.19491/j.issn.1001-9278.2024.06.005

中国塑料
中国塑料加工工业协会 轻工业塑料加工应用研究所 北京工商大学

中国塑料

CSTPCD北大核心
影响因子：0.574
ISSN：1001-9278
年,卷(期)：2024.38(6)