使用长链脂肪酸钠盐与芳基酰胺脂肪酸钠(SCAB)复配作为聚丙烯(PP)成核剂，研究了复配前后SCAB对PP结晶及力学性能的影响。结果表明，长碳链脂肪酸钠盐在复配过程和PP加工温度下均未改变SCAB的分子结构且复配可以明显改善SCAB分子间聚集状态;PP的结晶速率、缺口冲击强度和拉伸强度随着长链脂肪酸钠盐的碳链长度延长大幅提高且复配物未影响PP的晶体生长方式;硬脂酸钠复配的SCAB由于在PP基体中优异的分散性，能够更有效细化PP球晶，完善晶体结构，使其结晶速率提高6。3倍，缺口冲击强度提升27。3%，拉伸强度增长8。2 MPa。
Effect of long chain fatty acid sodium/sodium arylamide fatty acid compounding nucleating agent on properties of polypropylene
The sodium salt of long chain fatty acid and sodium of arylamide fatty acid were compounded to form a com-pounding nucleating agent(SCAB),and its effect on the crystallization and mechanical properties of polypropylene(PP)was investigated.The results indicated that the molecular structure of SCAB was not changed during its compounding process or at the processing temperature of PP,and its intermolecular aggregation state was significantly improved by the compounding process.The nucleated PP showed a significant increase in the crystallization rate,notch impact strength,and tensile strength with the extension of the carbon chain length of sodium salt of long chain fatty acid.The compound-ing did not affect the crystal growth mode of PP.Owing to the excellent dispersibility of SCAB in the PP matrix,a com-bination of SCAB with sodium stearate could refine the PP spherulites effectively and improve its crystal structure.This resulted in an increase in the crystallization rate of PP by 6.3 times,in the notch impact strength by 27.3%,and in the tensile strength by 8.2 MPa.

polypropylenelong chain fatty acid sodium saltsodium arylamide fatty acidcompoundingcrystallization propertymechanical property

董亚鹏、赵恬娇、王美珍、崔文举、林福华、王波

展开 >

太原科技大学化学工程与技术学院,太原 030024

太原科技大学环境与资源学院,太原 030024

山西工程科技职业大学交通工程学院,山西 晋中 030619

聚丙烯 长链脂肪酸钠盐 芳基酰胺脂肪酸钠 复配 结晶性能 力学性能

山西省科技成果转化引导专项山西省专利转化专项山西省高等学校科技创新计划山西省高等学校科技创新计划

2022040213010612023030102023L4212021L315

2024

10.19491/j.issn.1001-9278.2024.06.009

中国塑料
中国塑料加工工业协会 轻工业塑料加工应用研究所 北京工商大学

中国塑料

CSTPCD北大核心
影响因子：0.574
ISSN：1001-9278
年,卷(期)：2024.38(6)