采用4，4-氧代双苯磺酰肼(OBSH)作为发泡剂、以过氧化苯甲酰(BPO)作为交联剂、C9树脂作为增黏剂制备了乙烯-乙酸乙烯酯(EVA)发泡胶带，研究组分对2D发泡胶带使用性能的影响和机理。结果表明，在合适的EVA/BPO/OBSH/C9(100/3/3/40)条件下，发泡胶带能够在170℃和205℃下发泡。发泡胶带具有良好的使用性能，膨胀率超过2倍，不发生挂流，表面平整。同时，发泡胶带的拉伸强度高于5 MPa，断裂伸长率超过240%，吸水率低于5%。
Study on adhesive and foaming properties of EVA expandable tape for small volumes
This study prepared a series of ethylene-vinyl acetate(EVA)expandable tapes by using 4,4-oxobenzenesulfo-nyl hydrazine(OBSH)as foaming agent,benzoyl peroxide(BPO)as crosslinking agent,and C9 resin as a tackifier.The effect and mechanism of components on the performance of 2D foam tape were studied.The results indicated that,under the proper blending ratio of EVA/BPO/OBSH/C9(100/3/3/40),the expandable tape could be foamed at both 170℃and 205℃.The expansion rate of the expandable tape exceeded 2 times.And the surfaces of foams were smooth and without irreversible flowing.The tensile strength,the elongation at break and the water absorption of the expansion tape was 5 MPa,240%,and less than 5%,respectively.

expandable tapeethylene-vinyl acetate copolymeracoustic roughnesslow volatile organic compound4,4-oxobenzyl sulfonyl hydrazide

刘伟、余才利、陈小澄、张纯、赵克文

展开 >

贵州理工学院材料与能源工程学院,贵阳 550025

贵州永红航空机械有限责任公司,贵阳 550003

重庆迅昌汽车零部件有限公司,重庆 401120

发泡胶带 乙烯-乙酸乙烯酯共聚物 声振粗糙度 低挥发性有机化合物 4,4-氧代双苯磺酰肼

国家自然科学基金资助项目贵州省自然科学基金资助项目贵阳贵安人才培养项目

52263004黔科合基础-ZK[2022]一般179筑科合同[2024]2-12号

2024

10.19491/j.issn.1001-9278.2024.08.007

中国塑料
中国塑料加工工业协会 轻工业塑料加工应用研究所 北京工商大学

中国塑料

CSTPCD北大核心
影响因子：0.574
ISSN：1001-9278
年,卷(期)：2024.38(8)