首页|Preparation of modified epoxy resin with high hydrophobicity, low dielectric constant, toughness, and flame retardant by epoxy-functionalized siloxanes

Preparation of modified epoxy resin with high hydrophobicity, low dielectric constant, toughness, and flame retardant by epoxy-functionalized siloxanes

扫码查看
原文链接
  • NETL
  • NSTL
  • Elsevier
© 2024 Elsevier B.V.A series of α, ω-dimethylglycidoxypropyl-terminated PDMS oligomer (PDMS-GE) oligomers with different polymerization degrees were synthesized and used to modify the bisphenol-A diglycidyl ether E51 (DGEBA) / 4,4-diaminodiphenylmethane (DDM) epoxy resin, resulting in epoxy resins with high hydrophobicity, low dielectric constant, good impact toughness, low combustion heat release rate, and low total heat release. The combustion heat release rate and total heat release of the material decreased with the increase in the loadings of PDMS-GE. Relative to pure epoxy resin, the composite E51/D30–10, which using DGEBA as the matrix, PDMS-GE with a degree of polymerization of 30 as the modifier in an amount of 10 phr relative to the mass sum of DGEBA, PDMS-GE and DDM, exhibited the best comprehensive performance with a water contact angle of 102.42°, a dielectric strength of 6.49 kV/mm, a dielectric constant of 2.93 at 14.2 GHz, the peak rate of heat release (PRHR) and total heat release (THR) are of 378.3 kW/m2 and 134.4 MJ/m2, respectively. These comprehensive performances underscore the potential of PDMS-GE oligomers in significantly improving epoxy resin properties. When the loadings of PDMS-GE oligomers are less than 5 wt%, PDMS-GE with a lower degree of polymerization can improve the toughness of epoxy resins. The impact strength of the composite E51/D24–5, which uses DGEBA as the matrix, PDMS-GE with a degree of polymerization of 24 as the modifier in an amount of 5 phr relative to the mass sum of DGEBA, PDMS-GE, and DDM, reaches 98.1 kJ/m2, which is about 28.9 % higher than that of pure epoxy resin. The results also indicated that the degree of polymerization of PDMS-GE oligomers has less influence on the dielectric properties and mechanical properties of composite materials.

Allyl glycidyl etherDielectric propertiesEpoxy resinGlycidyl ether functionalized polydimethylsiloxane (PDMS-GE)HydrophobicityToughness

Zhang Y.、Shi Y.、Jin C.、Wu C.、Dong H.、Qu Z.、Song Y.

展开 >

College of Material Chemistry and Chemical Engineering Key Laboratory of Organosilicon Chemistry and Material Technology Ministry of Education Hangzhou Normal University

2025

10.1016/j.reactfunctpolym.2024.106114

Reactive & functional polymers

Reactive & functional polymers

SCI
ISSN：1381-5148
年,卷(期)：2025.207(Feb.)
  • 48